Originální abstrakt

The sintering and the microstructure of alumina and zirconia ceramics prepared by cold isostatic pressing of nanoceramic powders were studied. Ceramic powders contained 0, 1.5 and 3 mol.% of yttria. It was found that higher compacting pressures (700 MPa) yielded green bodies with smaller pores, which showed in their better sinterability. After sintering at 1100C, the bodies had a density exceeding 90% t.d. and grains below 80 nm. A critical ratio of the pore size in green bodies to the particle size was established, which enables sintering zirconia nanopowders of some 10 nm in size at a temperature of 1100C.

Vydáno

2003-01-01

Nakladatel

Faculty of Technology, University of Novi Sad

Místo

Novi Sad

ISBN

86-80995-46-0

Kniha

School of Ceramics, V Students' meeting

Strany od–do

38–

Počet stran

2

BIBTEX


@inproceedings{BUT11052,
  author="Petr {Dobšák} and Karel {Maca} and Martin {Trunec}",
  title="Sintering of alumina and zirconia nanoceramics",
  booktitle="School of Ceramics, V Students' meeting",
  year="2003",
  pages="2",
  publisher="Faculty of Technology, University of Novi Sad",
  address="Novi Sad",
  isbn="86-80995-46-0"
}